ABSTRACT
Introduction: Endodontically treated teeth are usually affected by extensive structure loss requiring the use of intraradicular posts to provide retention and restoration. Objective: An in vitro assessment was performed on the bonding of glass fiber posts to the root dentin. Material and method: Ninety (n = 10) single bovine roots were used in a 3 x 3 x 3 factorial study with subdivided plots: post customization varying the presence and type of resin (without customization, conventional resin, and Bulk Fill resin), light-curing device (Valo, Radii-Cal, Rainbow), and root third (cervical, middle, and apical). Result: For the customization factor, Tukey's test (5%) showed the superiority of the Bulk Fill (8.16 MPa) and Z350 (7.40 MPa) groups compared to the control group (4.92 MPa), without differing from each other. All light-curing devices differed, showing the superiority of Valo (9.36 MPa), Radii (6.96 MPa) as an intermediate, and the inferiority of Rainbow (4.17 MPa). The cervical root third (7.81 MPa) was superior, the apical third was inferior (5.80 MPa), and the middle third (6.88 MPa) was an intermediate without differing from the others. Conclusion: The customization of glass fiber posts increases the bond strength to the root dentin, regardless of the resin used. There was a compromise in the apical third and when using light-curing devices with lower light intensity.
Introdução: Dentes com extensa perda de estrutura podem comprometer a retenção das restaurações ao remanescente dental, onde pinos intraradiculares são indicados. Objetivo: Avaliou-se in vitro a união de pinos de fibra de vidro à dentina radicular em função de diferentes modos de reanatomização, fotopolimerizadores e regionalização radicular. Material e método: Noventa (n=10) raízes bovinas uniradiculares foram usadas num estudo fatorial 3 x 3 x 3 com parcelas subdivididas: Reanatomização do pino, variando a presença e tipo de resina (Sem reanatomização, Resina Convencional e Resina Bulkfill); Fotopolimerizador (Valo, Radii-cal, Rainbow); e Terço radicular (cervical, médio e apical). Resultado: O teste de Tukey (5%) evidenciou para o Fator Reanatomização superioridade dos grupos BulkFill (8.16MPa) e Z350 (7.40MPa) ao grupo Controle (4.92MPa), sem diferirem entre si. Todos os fotopolimerizadores diferiram entre si, com superioridade de Valo (9.36MPa), Radii (6.96MPa) intermediário, e inferioridade de Raiwbow (4.17MPa). O terço radicular cervical (7.81MPa) foi superior e o apical inferior (5.80MPa), com o terço médio (6.88MPa) intermediário e sem diferir dos demais. Conclusão: Conclui-se que a reanatomização de pinos de fibra de vidro aumenta a resistência de união à dentina radicular, independentemente da resina utilizada, havendo prejuízo no terço apical e quando são empregados fotopolimerizadores com menor intensidade luminosa.
Subject(s)
In Vitro Techniques , Cattle , Post and Core Technique , Resin Cements , Dentin , Light-Curing of Dental Adhesives , Photoinitiators, DentalABSTRACT
Objetivo: O objetivo foi avaliar a resistência de união de seis adesivos experimentais contendo sistemas fotoiniciadores binários ou ternários, associados a três diferentes concentrações de MDP (0-12% em peso) após 12 meses de armazenamento em água destilada. Material e Métodos: Adesivos experimentais foram preparados com: bis-GMA, UDMA, bis-EMA, TEGDMA, HEMA, BHT e etanol, contendo sistemas fotoiniciadores binários (CQ/amina) ou ternários (CQ/amina/DPIHFP 0,5% em peso). Foi adicionado a esta composição 0%, 6% ou 12% em peso de MDP. Os sistemas adesivos foram aplicados seguindo o protocolo com condicionamento ácido. Moldes cilíndricos transparentes foram colocados sobre a dentina hibridizada, preenchidos com resina composta e fotopolimerizados. Os corpos-de-prova foram armazenados em água destilada a 37oC por 24h ou 12 meses e submetidos ao ensaio de microcisalhamento (n=6). Os dados foram analisados por ANOVA de três fatores e teste de Tukey (α=5%). Resultados: Para o sistema binário, após 12 meses de armazenamento, todos os valores de resistência de união foram semelhantes. Em relação à degradação da resistência de adesão ao longo do tempo, as formulações de MDP de 6% e 12% mostraram resistência de união mais estável do que 0% de MDP. Para o sistema ternário, todas as formulações (0%, 6% e 12% em massa de MDP) mostraram resistência de união estável em função do tempo. Conclusão: Para o sistema binário, as concentrações de 6 e 12% em massa de MDP foram capazes de manter a resistência de união em função do tempo, enquanto que para o sistema ternário, a estabilidade de união foi obtida independentemente da concentração de MDP. Pode-se concluir que, para a formulação dos adesivos utilizados neste estudo, independente do sistema fotoiniciador, a concentração de 12% MDP apresentou valores de resistência de união mais estáveis após 12 meses de armazenamento em água (AU)
Objective: The aim was to evaluate the bond strength of six experimental adhesives containing binary or ternary photoinitiator systems, associated with three different MDP concentrations (0-12wt%) after 12 months of storage in distilled water. Material and Methods: Experimental adhesives were prepared with: bis-GMA, UDMA, bis-EMA, TEGDMA, HEMA, BHT, and ethanol, containing binary (CQ/amine) or ternary (CQ/amine/DPIHFP (diphenyliodonium hexafluorophosphate) 0.5wt%) photoinitiator systems. It was added to this composition 0wt%, 6wt%, or 12wt% of MDP. The adhesive systems were applied following the etch-and-rinse protocol. Transparent cylindrical molds were placed on the hybridized dentin, filled with composite resin and light-cured. The specimens were stored in distilled water at 37oC for 24h or 12 months and submitted to a microshear bond strength test (n=6). Data were analyzed by three-way ANOVA and Tukey's test (α=5%). Results: For the binary system, after 12 months of storage, all bond strength values were similar. Regarding bond strength degradation over time, 6wt% and 12wt% MDP formulations showed more stable bond strength than 0wt% MDP. For the ternary system, all formulations (0wt%, 6wt% and 12wt%) showed stable bond strength over time. Conclusion: For the binary photoinitiator system, the 6wt% and 12wt% MDP concentrations were able to keep bond strength stable over time, while for the ternary system, bond strength stability was achieved regardless the MDP concentration. (AU)
Subject(s)
Dental Cements , Photoinitiators, DentalABSTRACT
Abstract Camphorquinone is the most conventionally used photoinitiator in Dentistry. Although different alternative photoinitiators have been proposed, no photoinitiator was capable of completely substituting camphorquinone. The combination of photoinitiators has been considered the best alternative. Objectives: To evaluate the effect of combining Norrish type I and II photoinitiators on the cure efficiency of dental resin-based composites. Methodology: Experimental composites were produced containing different photoinitiator systems: Norrish type I-only, mono-alkyl phosphine oxide (TPO); Norrish type II-only, camphorquinone (CQ); or its combination, CQ and TPO, in a 1: 1 molar ratio. UV-vis absorption spectrophotometry was performed to assess the consumption of each photoinitiator after curing (n=3). A multi-wave LED (Bluephase® G2, Ivoclar Vivadent) was pre-characterized and used with a radiant exposure of 24 J/cm2. The degree of conversion was evaluated by Raman spectrometry, and the elution of the monomers by nuclear magnetic resonance analysis (n=3). Data were analyzed using ANOVA and Tukey's test (α=0.05; β=0.2). Results: The combination of CQ and TPO increased the consumption of the photoinitiator system compared to CQ-only (p=0.001), but presented similar consumption compared to TPO-only (p=0.52). There was no significant difference in the degree of conversion between the composites regardless of the photoinitiator system (p=0.81). However, the elution of the monomers was reduced when both photoinitiators were combined. TPO-based material presented the highest elution of monomers. Conclusions: The combination of the photoinitiator systems seems to be beneficial for the cure efficiency of dental resin-based composites.
Subject(s)
Composite Resins , Photoinitiators, Dental , Spectrophotometry , Materials Testing , ColorABSTRACT
Abstract Alternative photoinitiators with different absorption wavelengths have been used in resin composites (RCs), so it is crucial to evaluate the effectiveness of light-curing units (LCUs) on these products. Objective Using Fourier transform infrared analysis (FTIR) in vitro, the effects of varying radiant exposure (RE) values generated by second and third generation LED LCUs on the degree of conversion (DC) and maximum rate of polymerization (Rpmax) of an experimental Lucirin TPO-based RC were evaluated. Material and Methods 1 mm or 2 mm thick silicon molds were positioned on a horizontal attenuated total reflectance (ATR) unit attached to an infrared spectroscope. The RC was inserted into the molds and exposed to varying REs (18, 36 and 56 J/cm2) using second (Radii Plus, SDI) and third generation LED LCUs (Bluephase G2/Ivoclar Vivadent) or a quartz tungsten based LCU (Optilux 501/SDS Kerr). FTIR spectra (n=7) were recorded for 10 min (1 spectrum/s, 16 scans/spectrum, resolution 4 cm-1) immediately after their application to the ATR. The DC was calculated using standard techniques for observing changes in aliphatic to aromatic peak ratios both prior to, and 10 min after curing, as well as during each 1 second interval. DC and Rpmax data were analyzed using 3-way ANOVA and Tukey’s post-hoc test (p=0.05). Results No significant difference in DC or Rpmax was observed between the 1 mm or 2 mm thick specimens when RE values were delivered by Optilux 501 or when the 1 mm thick composites were exposed to light emitted by Bluephase G2, which in turn promoted a lower DC when 18 J/cm2 (13 s) were delivered to the 2 mm thick specimens. Radii Plus promoted DC and Rpmax values close to zero under most conditions, while the delivery of 56 J/cm2 (40 s) resulted in low DC values. Conclusions The third generation LCU provided an optimal polymerization of Lucirin TPO-based RC under most tested conditions, whereas the second generation LED-curing unit was useless regardless of the RE.
Subject(s)
Phosphines/radiation effects , Composite Resins/radiation effects , Light-Curing of Dental Adhesives/methods , Curing Lights, Dental , Radiation Dosage , Reference Values , Time Factors , Materials Testing , Reproducibility of Results , Analysis of Variance , Spectroscopy, Fourier Transform Infrared , Phase Transition , Photoinitiators, Dental/chemistry , Polymerization/radiation effectsABSTRACT
ABSTRACT Objective To evaluate the influence of phenyl-propanedione on yellowing and chemical-mechanical properties of experimental resin-based materials photoactivated using different light curing units (LCUs). Material and Methods Experimental resin-based materials with the same organic matrix (60:40 wt% BisGMA:TEGDMA) were mechanically blended using a centrifugal mixing device. To this blend, different photoinitiator systems were added in equimolar concentrations with aliphatic amine doubled by wt%: 0.4 wt% CQ; 0.38 wt% PPD; or 0.2 wt% CQ and 0.19 wt% PPD. The degree of conversion (DC), flexural strength (FS), Young’s modulus (YM), Knoop hardness (KNH), crosslinking density (CLD), and yellowing (Y) were evaluated (n=10). All samples were light cured with the following LCUs: a halogen lamp (XL 2500), a monowave LED (Radii), or a polywave LED (Valo) with 16 J/cm2. The results were analysed by two-way ANOVA and Tukey’s test (α=0.05). Results No statistical differences were found between the different photoinitiator systems to KNH, CLS, FS, and YM properties (p≥0.05). PPD/CQ association showed the higher DC values compared with CQ and PPD isolated systems when photoactivated by a polywave LED (p≤0.05). Y values were highest for the CQ compared with the PPD systems (p≤0.05). Conclusion PPD isolated system promoted similar chemical and mechanical properties and less yellowing compared with the CQ isolated system, regardless of the LCU used.